IDS Medical https://ids-vietnam.com Exclusive selection of high-end products Mon, 26 Oct 2015 00:16:23 +0000 en-US hourly 1 https://wordpress.org/?v=5.6.17 KERA® S-POWDER https://ids-vietnam.com/kera-s-powder/ Mon, 26 Oct 2015 00:15:53 +0000 http://ids-vietnam.com/?p=375 Continue reading ]]> KERA® S-POWDER – CoCr powder for laser-sintering
Approved for the most usual laser-sintering systems

Indications
– Ceramic veneered crowns and bridges
– Tertiary structures

Typical values

yield strength RP 0,2 % (MPa) 375
elongation (%) 14,7
young’s modul (GPa) 240
tensile strength (MPa) 525
density (g/cm3) 8,55
WAK
CTE (25 – 500°C)		 14,5
hardness (HV 10/30) 285*
Grain Size 10 – 45 μm (±5%)
type acc. DIN EN ISO 22674 ≥ Type 4 as
delivered

Lot numbers may show minimum deviation from typical values.
More information are available on our instruction for use.

Chemical Composition

Co Cr W Si Mn Fe Others
61,65 27,75 8,45 1,61 0,25 0,2 < 0,1
]]> KERA®-LINE https://ids-vietnam.com/kera-line/ Mon, 26 Oct 2015 00:04:56 +0000 http://ids-vietnam.com/?p=369 Continue reading ]]> KERA®-DISC – CoCr milling alloy

Indications
– Crowns and small bridges
– One piece Abutments
– Optimized for laser welding

Typical values

yield strength RP 0,2 % (MPa) 375
elongation (%) 14,7
young’s modul (GPa) 240
tensile strength (MPa) 525
density (g/cm3) 8,55
WAK
CTE (25 – 500°C)		 14,5
hardness (HV 10/30) 285*
dimensions (mm)   6,4 x 1000
8,0 x 1000
9,5 x 1000
12,0 x 1000
type acc. DIN EN ISO 22674 ≥ Type 4 as
delivered

Lot numbers may show minimum deviation from typical values.
More information are available on our instruction for use.

Chemical Composition

Co Cr W Si Mn Fe Others
61,65 27,75 8,45 1,61 0,25 0,2 < 0,1
]]> KERA®-DISC https://ids-vietnam.com/kera-disc/ Mon, 26 Oct 2015 00:06:56 +0000 http://ids-vietnam.com/?p=372 Continue reading ]]> KERA®-DISC – CoCr milling alloy

Indications
– Crowns and bridges
– One piece Abutments
– Implant retained suprastructures
– Optimized for laser welding

Typical values

yield strength RP 0,2 % (MPa) 375
elongation (%) 14,7
young’s modul (GPa) 240
tensile strength (MPa) 525
density (g/cm3) 8,55
WAK
CTE (25 – 500°C)		 14,5
hardness (HV 10/30) 285*
dimensions (mm)
(X) = 8/10/12/13,5/14/15/16/17,5/18/20/24,5		 Ø 98,3 x (X)
Ø 99,5 x (X)
type acc. DIN EN ISO 22674 ≥ Type 4 as
delivered

* with appropriate sample preparation

Lot numbers may show minimum deviation from typical values.
More information are available on our instruction for use.

Chemical Composition

Co Cr W Si Mn Fe Others
61,65 27,75 8,45 1,61 0,25 0,2 < 0,1
]]> KERA® TI 5-DISC https://ids-vietnam.com/kera-ti-5-disc/ Mon, 26 Oct 2015 00:03:24 +0000 http://ids-vietnam.com/?p=366 Continue reading ]]> KERA®Ti 5-DISC – Biocompatible titanium-milling alloy

Indications
– Crowns and bridges
– One piece abutments
– Implant retained suprastructures

Typical values

yield strength RP 0,2 % (MPa) >760
elongation (%) >8
tensile strength (MPa) >825
density (g/cm3) 4,4
WAK
CTE (25 – 500°C)		 ∼ 10,0
hardness (HV 10/30) ∼ 310*
dimensions (mm)
(X) = 8/10/12/14/15/16/18/20/25/27		 Ø 98,5 x (X)
Ø 99,5 x (X)

* with appropriate sample preparation

Lot numbers may show minimum deviation from typical values.
More information are available on our instruction for use.

Chemical Composition

Ti Al V Others
89,0 6,4 4,1 < 0,1
]]> TENER IT https://ids-vietnam.com/tener-it/ Sun, 25 Oct 2015 23:56:15 +0000 http://ids-vietnam.com/?p=363 Continue reading ]]> TENER IT – Partial denture alloy with extra reduced content of carbon and good polishing properties

Indications
– One piece casting
– Implant bars
– Attachments
– Optimized for laser welding

Typical values

yield strength RP 0,2 % (MPa) 555
elongation (%) 8,6
young’s modul (GPa) 185
tensile strength (MPa) 745
density (g/cm3) 8,3
casting temperature (°C) 1504
WAK
CTE (25 – 500°C)		 not relevant
hardness (HV 10/30) 330
dimensions (mm) Ø 8 x 15
type acc. DIN EN ISO 22674 ≥ Type 5 as
delivered

Lot numbers may show minimum deviation from typical values.
More information are available on our instruction for use.

Chemical Composition

Co Cr Mo W Fe Mn Si C Others
62,75 28,7 5,85 0,75 0,5 0,5 0,45 0,15 < 0,1
]]> TENER 350 https://ids-vietnam.com/tener-350/ Sun, 25 Oct 2015 23:54:41 +0000 http://ids-vietnam.com/?p=360 Continue reading ]]> TENER 350® – Partial denture alloy with high strength

Indications
– Filigree palatal coverages
– Implant bars
– Attachments

Typical values

yield strength RP 0,2 % (MPa) > 500
elongation (%) > 2
young’s modul (GPa) > 150
tensile strength (MPa) 800
density (g/cm3) 8,3
casting temperature (°C) 1520
WAK
CTE (25 – 500°C)		 not relevant
hardness (HV 10/30) < 450
dimensions (mm) Ø 8 x 15
type acc. DIN EN ISO 22674 ≥ Type 5 as
delivered

Lot numbers may show minimum deviation from typical values.
More information are available on our instruction for use.

Chemical Composition

Co Cr Mo W Fe Si Mn Others
62 29,3 5,8 0,7 0,6 0,5 0,5 < 0,1
]]> DENTIUM https://ids-vietnam.com/dentium/ Sun, 25 Oct 2015 23:52:36 +0000 http://ids-vietnam.com/?p=357 Continue reading ]]> DENTIUM – Sturdy partial denture alloy for gracile structures

Indications
– Filigree palatal coverages
– Implant bars
– Attachments

Typical values

yield strength RP 0,2 % (MPa) 590
elongation (%) 2,8
young’s modul (GPa) 155
tensile strength (MPa) 850
density (g/cm3) 8,25
casting temperature (°C) 1480
WAK
CTE (25 – 500°C)		 nicht
hardness (HV 10/30) 460
dimensions (mm) Ø 8 x 15
type acc. DIN EN ISO 22674 ≥ Type 5 as
delivered

Lot numbers may show minimum deviation from typical values.
More information are available on our instruction for use.

Chemical Composition

Co Cr Mo Mn C Si Fe Others
61,3 30,15 5,5 0,6 0,65 1 0,63 < 0,1
]]> ROBUR 400 https://ids-vietnam.com/robur-400/ Sun, 25 Oct 2015 23:50:33 +0000 http://ids-vietnam.com/?p=354

ROBUR 400® – Partial denture alloy with excellent spring-hard properties

Indications
– Partial denture with clips
– Implant bars
– Attachments

Typical values

yield strength RP 0,2 % (MPa) 705
elongation (%) 2,6
young’s modul (GPa) 185
tensile strength (MPa) 930
density (g/cm3) 8,3
casting temperature (°C) 1490
WAK
CTE (25 – 500°C)		 not relevant
hardness (HV 10/30) 420
dimensions (mm) Ø 8 x 15
type acc. DIN EN ISO 22674 ≥ Type 5 as
delivered

Lot numbers may show minimum deviation from typical values.
More information are available on our instruction for use.

Chemical Composition

Co Cr Mo Fe W Mn C Si Others
62,5 28,5 6,1 0,7 0,6 0,55 0,5 0,45 < 0,1
]]> MAIN METALL https://ids-vietnam.com/main-metall/ Sun, 25 Oct 2015 23:46:10 +0000 http://ids-vietnam.com/?p=351

Main Metall – CoCr alloy for high demands

Indications
– Wide span ceramic veneered restorations
– Implant retained restorations
– Combinated restorations

Typical values

yield strength RP 0,2 % (MPa) 570
elongation (%) 4,2
young’s modul (GPa) 190
tensile strength (MPa) 725
density (g/cm3) 8,7
casting temperature (°C) 1474
WAK
CTE (25 – 500°C)		 14,0
hardness (HV 10/30) 370
dimensions (mm) Ø 8 x 15
type acc. DIN EN ISO 22674 ≥ Type 5 as 
delivered

Lot numbers may show minimum deviation from typical values.
More information are available on our instruction for use.

Chemical Composition

Co Cr W Nb Mo Si V Others
60,2 25,25 9 2,2 1,05 1 1 < 0,1
]]> FireCam HD https://ids-vietnam.com/firecam-hd/ Sun, 25 Oct 2015 07:54:20 +0000 http://ids-vietnam.com/?p=332

The full-featured FireCam HD from 3DISC Imaging rapidly delivers high-
definition intraoral images during consultations, enhancing chairside 
time with patients.

High Resolution Camera

Advancements in camera technology have allowed us to fit an incredibly high amount of pixels into the FireCam HD. The image resolution of 5M pixels is the highest on the market and enables you to see every detail while examining the patients’ teeth.

Automatic Optimal Adjustment

The FireCam HD has auto-focus and auto-brightness, giving you the best possible image. This allows dentists to focus on the patient instead of dealing with hardware settings.

Anti-Fog and Easy to Sterilize

A specially designed heating mechanism prevents lens fog from patient respiration, which causes blurry and unclear images. Insert the FireCam HD in a thin sheath to cover the seamless and smooth exterior, which is easily strerilized after use.

Slim Design for Comfort

Sized as a common dental instrument, the compact design of the FireCam HD fits naturally into the hand of the dentist. The slim design also makes it a more pleasant experience for the patient. Equipped with a 3 meter cable so you are able to move freely.

Document and Motivate Progress

Use the FireCam HD during consultations to show patients a clear image of oral issues. Document patients’ issues before starting treatment and register the progress. Motivate patients to further treatment and encourage changes in oral hygiene habits.

]]>