METAL – IDS Medical https://ids-vietnam.com Exclusive selection of high-end products Mon, 26 Oct 2015 00:16:23 +0000 en-US hourly 1 https://wordpress.org/?v=5.6.17 KERA® S-POWDER https://ids-vietnam.com/kera-s-powder/ Mon, 26 Oct 2015 00:15:53 +0000 http://ids-vietnam.com/?p=375 Continue reading ]]> KERA® S-POWDER – CoCr powder for laser-sintering
Approved for the most usual laser-sintering systems

Indications
– Ceramic veneered crowns and bridges
– Tertiary structures

Typical values

yield strength RP 0,2 % (MPa) 375
elongation (%) 14,7
young’s modul (GPa) 240
tensile strength (MPa) 525
density (g/cm3) 8,55
WAK
CTE (25 – 500°C)		 14,5
hardness (HV 10/30) 285*
Grain Size 10 – 45 μm (±5%)
type acc. DIN EN ISO 22674 ≥ Type 4 as
delivered

Lot numbers may show minimum deviation from typical values.
More information are available on our instruction for use.

Chemical Composition

Co Cr W Si Mn Fe Others
61,65 27,75 8,45 1,61 0,25 0,2 < 0,1
]]> KERA®-LINE https://ids-vietnam.com/kera-line/ Mon, 26 Oct 2015 00:04:56 +0000 http://ids-vietnam.com/?p=369 Continue reading ]]> KERA®-DISC – CoCr milling alloy

Indications
– Crowns and small bridges
– One piece Abutments
– Optimized for laser welding

Typical values

yield strength RP 0,2 % (MPa) 375
elongation (%) 14,7
young’s modul (GPa) 240
tensile strength (MPa) 525
density (g/cm3) 8,55
WAK
CTE (25 – 500°C)		 14,5
hardness (HV 10/30) 285*
dimensions (mm)   6,4 x 1000
8,0 x 1000
9,5 x 1000
12,0 x 1000
type acc. DIN EN ISO 22674 ≥ Type 4 as
delivered

Lot numbers may show minimum deviation from typical values.
More information are available on our instruction for use.

Chemical Composition

Co Cr W Si Mn Fe Others
61,65 27,75 8,45 1,61 0,25 0,2 < 0,1
]]> KERA®-DISC https://ids-vietnam.com/kera-disc/ Mon, 26 Oct 2015 00:06:56 +0000 http://ids-vietnam.com/?p=372 Continue reading ]]> KERA®-DISC – CoCr milling alloy

Indications
– Crowns and bridges
– One piece Abutments
– Implant retained suprastructures
– Optimized for laser welding

Typical values

yield strength RP 0,2 % (MPa) 375
elongation (%) 14,7
young’s modul (GPa) 240
tensile strength (MPa) 525
density (g/cm3) 8,55
WAK
CTE (25 – 500°C)		 14,5
hardness (HV 10/30) 285*
dimensions (mm)
(X) = 8/10/12/13,5/14/15/16/17,5/18/20/24,5		 Ø 98,3 x (X)
Ø 99,5 x (X)
type acc. DIN EN ISO 22674 ≥ Type 4 as
delivered

* with appropriate sample preparation

Lot numbers may show minimum deviation from typical values.
More information are available on our instruction for use.

Chemical Composition

Co Cr W Si Mn Fe Others
61,65 27,75 8,45 1,61 0,25 0,2 < 0,1
]]> KERA® TI 5-DISC https://ids-vietnam.com/kera-ti-5-disc/ Mon, 26 Oct 2015 00:03:24 +0000 http://ids-vietnam.com/?p=366 Continue reading ]]> KERA®Ti 5-DISC – Biocompatible titanium-milling alloy

Indications
– Crowns and bridges
– One piece abutments
– Implant retained suprastructures

Typical values

yield strength RP 0,2 % (MPa) >760
elongation (%) >8
tensile strength (MPa) >825
density (g/cm3) 4,4
WAK
CTE (25 – 500°C)		 ∼ 10,0
hardness (HV 10/30) ∼ 310*
dimensions (mm)
(X) = 8/10/12/14/15/16/18/20/25/27		 Ø 98,5 x (X)
Ø 99,5 x (X)

* with appropriate sample preparation

Lot numbers may show minimum deviation from typical values.
More information are available on our instruction for use.

Chemical Composition

Ti Al V Others
89,0 6,4 4,1 < 0,1
]]> TENER 350 https://ids-vietnam.com/tener-350/ Sun, 25 Oct 2015 23:54:41 +0000 http://ids-vietnam.com/?p=360 Continue reading ]]> TENER 350® – Partial denture alloy with high strength

Indications
– Filigree palatal coverages
– Implant bars
– Attachments

Typical values

yield strength RP 0,2 % (MPa) > 500
elongation (%) > 2
young’s modul (GPa) > 150
tensile strength (MPa) 800
density (g/cm3) 8,3
casting temperature (°C) 1520
WAK
CTE (25 – 500°C)		 not relevant
hardness (HV 10/30) < 450
dimensions (mm) Ø 8 x 15
type acc. DIN EN ISO 22674 ≥ Type 5 as
delivered

Lot numbers may show minimum deviation from typical values.
More information are available on our instruction for use.

Chemical Composition

Co Cr Mo W Fe Si Mn Others
62 29,3 5,8 0,7 0,6 0,5 0,5 < 0,1
]]> DENTIUM https://ids-vietnam.com/dentium/ Sun, 25 Oct 2015 23:52:36 +0000 http://ids-vietnam.com/?p=357 Continue reading ]]> DENTIUM – Sturdy partial denture alloy for gracile structures

Indications
– Filigree palatal coverages
– Implant bars
– Attachments

Typical values

yield strength RP 0,2 % (MPa) 590
elongation (%) 2,8
young’s modul (GPa) 155
tensile strength (MPa) 850
density (g/cm3) 8,25
casting temperature (°C) 1480
WAK
CTE (25 – 500°C)		 nicht
hardness (HV 10/30) 460
dimensions (mm) Ø 8 x 15
type acc. DIN EN ISO 22674 ≥ Type 5 as
delivered

Lot numbers may show minimum deviation from typical values.
More information are available on our instruction for use.

Chemical Composition

Co Cr Mo Mn C Si Fe Others
61,3 30,15 5,5 0,6 0,65 1 0,63 < 0,1
]]> ROBUR 400 https://ids-vietnam.com/robur-400/ Sun, 25 Oct 2015 23:50:33 +0000 http://ids-vietnam.com/?p=354

ROBUR 400® – Partial denture alloy with excellent spring-hard properties

Indications
– Partial denture with clips
– Implant bars
– Attachments

Typical values

yield strength RP 0,2 % (MPa) 705
elongation (%) 2,6
young’s modul (GPa) 185
tensile strength (MPa) 930
density (g/cm3) 8,3
casting temperature (°C) 1490
WAK
CTE (25 – 500°C)		 not relevant
hardness (HV 10/30) 420
dimensions (mm) Ø 8 x 15
type acc. DIN EN ISO 22674 ≥ Type 5 as
delivered

Lot numbers may show minimum deviation from typical values.
More information are available on our instruction for use.

Chemical Composition

Co Cr Mo Fe W Mn C Si Others
62,5 28,5 6,1 0,7 0,6 0,55 0,5 0,45 < 0,1
]]> MAIN METALL https://ids-vietnam.com/main-metall/ Sun, 25 Oct 2015 23:46:10 +0000 http://ids-vietnam.com/?p=351

Main Metall – CoCr alloy for high demands

Indications
– Wide span ceramic veneered restorations
– Implant retained restorations
– Combinated restorations

Typical values

yield strength RP 0,2 % (MPa) 570
elongation (%) 4,2
young’s modul (GPa) 190
tensile strength (MPa) 725
density (g/cm3) 8,7
casting temperature (°C) 1474
WAK
CTE (25 – 500°C)		 14,0
hardness (HV 10/30) 370
dimensions (mm) Ø 8 x 15
type acc. DIN EN ISO 22674 ≥ Type 5 as 
delivered

Lot numbers may show minimum deviation from typical values.
More information are available on our instruction for use.

Chemical Composition

Co Cr W Nb Mo Si V Others
60,2 25,25 9 2,2 1,05 1 1 < 0,1
]]> KERA-NH https://ids-vietnam.com/kera-nh/ Thu, 22 Oct 2015 09:09:34 +0000 http://ids-vietnam.com/?p=321

KERA®NH – NiCr alloy for universal requirements

Indications
– Ceramic veneered crowns and smaller bridges
– Telescopic crowns
– Attachments
– Full metal crowns

Typical values

yield strength RP 0,2 % (MPa) 380
elongation (%) 11,5
young’s modul (GPa) 135
tensile strength (MPa) 560
density (g/cm3) 8,2
casting temperature (°C) 1430
WAK
CTE (25 – 500°C)		 14,0
hardness (HV 10/30) 240
dimensions (mm) Ø 8 x 15
type acc. DIN EN ISO 22674 ≥ Type 3 as
delivered

Lot numbers may show minimum deviation from typical values.
More information are available on our instruction for use.

]]> KERA-N https://ids-vietnam.com/kera-n/ Thu, 22 Oct 2015 09:05:50 +0000 http://ids-vietnam.com/?p=318

KERA N® – NiCr alloy for the daily use

Indications
– Ceramic veneered crowns and smaller bridges
– Telescopic crowns
– Full metal crowns

Typical values

yield strength RP 0,2 % (MPa) 340
elongation (%) 26,5
young’s modul (GPa) 125
tensile strength (MPa) 550
density (g/cm3) 8,43
casting temperature (°C) 1450
WAK
CTE (25 – 500°C)		 14,1
hardness (HV 10/30) 185
dimensions (mm) Ø 8 x 15
type acc. DIN EN ISO 22674 ≥ Type 3 as
delivered

Lot numbers may show minimum deviation from typical values.
More information are available on our instruction for use.

]]>